牌號(hào)
|
30CrMnSiNi2A合金結(jié)構(gòu)鋼絲
|
|
|
|
|
|
|
|
|
中國ISC
|
A45303
|
|
|
|
|
|
|
|
|
對(duì)應(yīng)標(biāo)準(zhǔn)
|
GB /T 3079-1993
|
|
|
|
|
|
|
|
|
合金結(jié)構(gòu)鋼絲
|
|
|
|
|
|
|
|
|
Alloy structure steels wires
|
|
|
|
|
|
|
|
|
歸類
|
合金鋼
|
|
|
|
|
|
|
|
|
30CrMnSiNi2A 化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
|
最小值
|
0.27
|
0.9
|
1
|
-
|
-
|
0.9
|
1.4
|
-
|
|
最大值
|
0.34
|
1.2
|
1.3
|
0.025
|
0.025
|
1.2
|
1.8
|
0.25
|
|
特級(jí)優(yōu)質(zhì)鋼 P≤0.025%，S≤0.015%，此時(shí)在鋼號(hào)后加E。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GB 30CrMnSiNi2A GB/T 3079 Mechanical
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Yield
|
Tensile
|
Impact
|
Elongation
|
Reduction in cross section on fracture
|
As-Heat-Treated Condition
|
Brinell hardness (HBW)
|
|
|
|
Rp0.2 (MPa)
|
Rm (MPa)
|
KV/Ku (J)
|
A (%)
|
Z (%)
|
|
|
|
595 (≥)
|
376 (≥)
|
23
|
12
|
31
|
Solution and Aging, Annealing, Ausaging, Q+T,etc
|
242
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GB 30CrMnSiNi2A GB/T 3079 Physical
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GB 30Cr Mn Si Ni2A GB/T 3079的物理性能主要包括彈性模量、熱膨脹系數(shù)、導(dǎo)熱系數(shù)、比熱容、電阻值、密度、泊松比等。
|
|
|
|
|
|
|
|
|
|
Temperature
|
Modulus of elasticity
|
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and
|
Thermal conductivity
|
Specific thermal capacity
|
Specific electrical resistivity
|
Density
|
Poisson’s coefficient, ν
|
|
|
(°C)
|
(GPa)
|
(W/m·°C)
|
(J/kg·°C)
|
(Ω mm2/m)
|
(kg/dm3)
|
|
|
24
|
-
|
-
|
|
|
0.31
|
-
|
|
|
|
953
|
185
|
-
|
24.3
|
312
|
|
-
|
|
|
|
531
|
-
|
11
|
22.2
|
|
|
112
|
244
|
|
|
|
|
|
|
|
|
|
|
|
|
GB 30CrMnSiNi2A GB/T 3079 Processing Service
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|